Why Is My Solder Joint Not Shiny. The most common causes are a. Or, when i solder a joint (maybe with the. Type of metal used, type of flux used,. If the solder cools very quickly. There are many things that can effect the shinyness of the joint, including but not limited to: Adding too much solder to a joint during the soldering process can be just as significant of an issue as underapplying solder. I can see my reflection in. If the solder joint is receding (pulling back) from either the pin or pad, the joint is not acceptable. It will look a little beaded up instead of having formed a nice miniscus with the edges having flowed along the metal of the joint. If i do the solder joint super quick it will look really shiny for a short while and then suddenly go extremely dull. When a solder joint is reheated without applying flux, the solder might get dull. My joints are silvery and smooth, sometimes with a small area of tiny ripple (i don't know if it's what they call grainy). If your solder joints are not shiny, but a have a duller finish, it is typically just the effect of having a coarse grainy structure in the.
from www.circuitbasics.com
I can see my reflection in. It will look a little beaded up instead of having formed a nice miniscus with the edges having flowed along the metal of the joint. When a solder joint is reheated without applying flux, the solder might get dull. If i do the solder joint super quick it will look really shiny for a short while and then suddenly go extremely dull. Adding too much solder to a joint during the soldering process can be just as significant of an issue as underapplying solder. Type of metal used, type of flux used,. If the solder cools very quickly. Or, when i solder a joint (maybe with the. The most common causes are a. There are many things that can effect the shinyness of the joint, including but not limited to:
Tips for Good Soldering Technique Circuit Basics
Why Is My Solder Joint Not Shiny If your solder joints are not shiny, but a have a duller finish, it is typically just the effect of having a coarse grainy structure in the. There are many things that can effect the shinyness of the joint, including but not limited to: It will look a little beaded up instead of having formed a nice miniscus with the edges having flowed along the metal of the joint. The most common causes are a. I can see my reflection in. Or, when i solder a joint (maybe with the. If i do the solder joint super quick it will look really shiny for a short while and then suddenly go extremely dull. If the solder joint is receding (pulling back) from either the pin or pad, the joint is not acceptable. My joints are silvery and smooth, sometimes with a small area of tiny ripple (i don't know if it's what they call grainy). If your solder joints are not shiny, but a have a duller finish, it is typically just the effect of having a coarse grainy structure in the. Adding too much solder to a joint during the soldering process can be just as significant of an issue as underapplying solder. Type of metal used, type of flux used,. When a solder joint is reheated without applying flux, the solder might get dull. If the solder cools very quickly.